LNP STAT-LOY PC 63000TXB

?	特点：LNP* Stat-Loy* PC 63000TXB 是一个具有*性防静电特性的聚碳酸酯/聚酯树脂产品，新增的功能包括：透明，制定FDA与食品接触的添加剂，ISO 10993 Bioassessed。 
?	LNP STAT-LOY PC 63000TXB



LNP? STAT-LOY? Compound PC 63000TXB
 
Also known as:LNP? Stat-loy? Compound 63000TXB Product reorder name:63000TXB
LNP* Stat-Loy* 63000TXB is a product based on Polycarbonate/Polyester resin featuring a permanent anti-static characteristic. Added features include: Transparent, Formulated with FDA Food Contact Additives and Bioassessed to ISO 10993.
 
Property
TYPICAL PROPERTIES(1)
MECHANICAL	Value	Unit	Standard
Tensile Stress,brk,Type I,5mm/min	360	kgf/cm2	ASTM D 638
Tensile Strain,yld,Type I,5mm/min	5	%	ASTM D 638
Tensile Modulus,5mm/min	12800	kgf/cm2	ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span	500	kgf/cm2	ASTM D 790
Flexural Modulus,1.3mm/min,50mm span	12400	kgf/cm2	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact,unnotched,23℃	147	cm-kgf/cm	ASTM D 4812
Izod Impact,notched,23℃	85	cm-kgf/cm	ASTM D 256
THERMAL	Value	Unit	Standard
HDT,1.82 MPa,3.2mm,unannealed	71	℃	ASTM D 648
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.15	-	ASTM D 792
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	1.E+10-1.E+12	Ohm-cm	ASTM D 257
Surface Resistivity	1.E+10-1.E+12	Ohm	ASTM D 257
Static Decay,5000V to <50V	<2	< seconds	FTMS101B
Source GMD,last updated:2011/06/27
Parameter Injection Molding	Value	Unit
Drying Temperature	70-80	℃
Drying Time	4	hrs
Maximum Moisture Content	0.05-0.1	%
Melt Temperature	200-210	℃
Front-Zone 3 Temperature	205-215	℃
Middle-Zone 2 Temperature	195-205	℃
Rear-Zone 1 Temperature	180-195	℃
Mold Temperature	10-50	℃
Back Pressure	0.2-0.3	MPa
Screw Speed	30-60	rpm